tempering temperature的意思

tempering temperature中文翻譯：

[機]回火溫度

相似詞語短語

tempering───v.調和（temper的ing形式）；n.[機]回火

temperature───n.溫度；體溫；氣溫；發燒

tempering top───回火頂

critical temperature───[物][電子]臨界溫度；n.臨界溫度

temperature outside───室外溫度

temperature rise───[電]溫升；溫度上升；溫度上升，溫升，升溫

constant temperature───[熱]恒溫；定溫；等溫；等溫，恒溫

fluctuating temperature───波動溫度；脈動溫度；脈動溫度，波動溫度

low temperature───低溫，低溫度；[物]低溫

雙語使用場景

tempering temperature, the retained austenite decreases.───回火溫度升高，其殘余奧氏體量逐漸減少。

When tempering temperature further heightens, he hardness descends gradually.───當回火溫度進一步升高時，硬度逐漸降低。

The hardenability is irrelevant to the isothermal tempering temperature.───淬透性與等溫回火溫度無關。

The tempered lath martensite grows up with the tempering temperature increasing, however the tendency of growing is not obvious.───隨淬火加熱溫度的升高，板條馬氏體逐漸長大，但長大趨勢不明顯；

With the elevating of the tempering temperature, the hardness can be increased and the wear resistance will be decreased.───隨著回火溫度的提高，深冷處理后的試樣硬度升高，但耐磨性降低。

After tempering, the hardness and antibacterial property first increase then decrease with the increase of tempering temperature.───回火后，隨回火溫度的升高，硬度和抗菌率均呈先增大后減小的趨勢；

the higher the tempering temperature, the lower the strength and hardness, and the better the plasticity and toughness are.───隨著回火溫度的升高，合金的強度、硬度越低，塑性、韌性越好。

With increasing tempering temperature, the retained austenite decreases.───回火溫度升高，其殘余奧氏體量逐漸減少。

The results show that quenching temperature, tempering temperature and holding time are determining factors.───結果表明：加熱溫度、回火溫度、保溫時間起著決定性作用；

英語使用場景

For acquiring good properties of brazed joint of coal cutter, the effect of tempering temperature on microstructure and shearing strength of brazed joint was studied.

Effects of tempering temperature on high carbon medium manganese steel has been investigated in present work.

Having studied the relationship between tempered hardness and tempering temperature for hardened carbon steels, a tempering behaviour model is set up between hardness and temperature.

The relationship between impact toughness and tempering temperature indicated secondary tempering brit - tleness peak at between 570 - 580.

Microalloy element V should be avoided adding , although it improves the strength at elevated tempering temperature , but reduces the ductility .